Chimi, Yasuhiro; Sato, Kenji*; Kasahara, Shigeki; Umehara, Ryuji*; Hata, Kuniki; Hanawa, Satoshi; Nishiyama, Yutaka
no journal, ,
To investigate the influence of Zinc (Zn) injection on primary water stress corrosion cracking (PWSCC) growth behavior, crack growth tests of 10% cold-worked Alloy 600 in simulated primary water environment of pressurized water reactor (PWR) at 320C and 360C, with and without Zn injection, under dissolved hydrogen (DH) conditions of 5, 30, and 50 cc/kgHO. As a result of the crack growth tests at 360C, it is implied that Zn injection suppresses the oxidation inside the crack and the crack growth rate (CGR). From the crack growth tests at 320C with Zn injection, DH-dependence of CGR showed a similar tendency to the predicted CGR based on the CGR data without Zn injection. Obvious influence of Zn injection on DH-dependence of CGR at 320C was not observed in the present study.